Extremely soft fit: Seal with a light touch, zero gap on curved surfaces
High resilience: It rebounds when flattened and does not collapse even after long-term use
Skin-friendly and safe: Soft touch, can be directly in contact with the skin
Flame-retardant and lightweight: Self-extinguishing when removed from the fire source, soft and light
The halogen content has been significantly reduced to below 1500ppm, far exceeding the industry's environmental protection standards
The tear resistance strength is significantly enhanced compared with traditional products, and the wear resistance is excellent
It exhibits excellent bonding properties with various substrates such as metal and plastic
It is resistant to mineral oil, lubricating oil, acid and alkali media, with an extremely small volume change rate
UL94-V0 flame retardant grade, self-extinguishing when removed from the fire source, suitable for scenarios with high fire protection requirements
Performance | Testing method | Typical value |
Product | / | TYC-150U |
Color | 目测 | 黑色 |
Density（kg/m3） | ASTM D3574 | 110 |
Hardness（shore C） | ASTM D2240 | 10 |
Thickness（mm） | ASTM D374/D374M | 0.5~32 |
Compression set （%） (20%, 70℃, 22h) | ASTM D1056 | ≤30 |
25% compressive strength （kPa） | ASTM D1056 | 30 |
High-temperature shrinkage rate（70℃ 22h）(%) | ASTM D1056 | ≤5 |
Tensile strength（kPa, min） | ASTM D412 | 330 |
Elongation at break（%, min） | ASTM D412 | 100 |
Tear strength（N/mm） | ASTM D624 | ≥ 1 |
Water absorption rate（%） | ASTM D1056 | / |
Thermal conductivity（W/(m·K)） | ASTM E1461 | ≤0.06 |
Volume resistance (Ω·cm） | ASTM D257 | ≥ 109 |
Flame retardant grade | UL 94 | V-0 |
Temperature resistance range (℃) | SAE J-2236 | -40~100 |